China High Alumina Insulating Brick

$SK40 Insulating Refractory Brick Yellow Al2O3 High Alumina Brick$

SK40 Insulating Refractory Brick Yellow Al2O3 High Alumina Brick

Shape:Brick

Al2o3 content (%):48%-85%

Refractoriness (degree):Common (1580°< Refractoriness< 1770°)
Boiler Furnace High Alumina Insulating Brick Lightweight Slag Resistance

Cold Crushing Strength:≥4.5 MPa

Linear Change on Reheating，（5h,≤2%）:≥1400 ℃

Thermal conductivity（350±25）℃:≤0.55 W/m·K
$Corundum Refractory Alumina Magnesia Spinel Brick For Industry Furance$

Corundum Refractory Alumina Magnesia Spinel Brick For Industry Furance

Cold Crushing Strength:≥4.5 MPa

Linear Change on Reheating，（5h,≤2%）:≥1400 ℃

Thermal conductivity（350±25）℃:≤0.55 W/m·K
Thermal Insulation Al2O3 95% Alumina Ceramic Brick 3.0MPa

Cold Crushing Strength:≥3.0 MPa

Linear Change on Reheating，（5h,≤2%）:≥1400 ℃

Thermal conductivity（350±25）℃:≤0.35 W/m·K
$Mullite High Alumina Insulating Brick Kilns Refractory Fire Brick Heat Insulation$

Mullite High Alumina Insulating Brick Kilns Refractory Fire Brick Heat Insulation

Bulk Density:≤0.8 g/cm3

Cold Crushing Strength:≥3.0 MPa

Linear Change on Reheating，（5h,≤2%）:≥1400 ℃
$Furnace Refractory High Alumina Insulating Brick Thermal Processing$

Furnace Refractory High Alumina Insulating Brick Thermal Processing

Al203:≥36%

Fe2o3:≤1.0

Bulik density:≤1.05 g/m³
Heat Insulation 1350C 0.7g/Cm3 Fire Retardant Bricks

Bulk Density:≤0.7 g/cm3

Cold Crushing Strength:≥2.0 MPa

Linear Change on Reheating，（5h,≤2%）:≥1350 ℃
Wear Resistance 0.7g/Cm3 High Alumina Insulating Brick

Bulk Density:≤0.7 g/cm3

Linear Change on Reheating，（5h,≤2%）:≥1350 ℃

Characteristic 1:Light weight
High Alumina Light Weight 0.8g Pizza Oven Fire Bricks

Bulk Density:≤0.8 g/cm3

Cold Crushing Strength:≥3.0 MPa

Linear Change on Reheating，（5h,≤2%）:≥1400 ℃
Industry Furnace 1.2g 1400C High Alumina Insulating Brick

Bulk Density:≤1.2 g/cm3

Cold Crushing Strength:≥4.5 MPa

Linear Change on Reheating，（5h,≤2%）:≥1400 ℃
High Strength Cement Kiln 48 Al2O3 High Heat Bricks

Bulk Density:≤1.2 g/cm3

Cold Crushing Strength:≥4.5 MPa

Thermal conductivity（350±25）℃:≤0.55 W/m·K
1770℃ 2.0 Fe2O3 High Alumina Insulating Brick For Coke Oven

Cold Crushing Strength:≥4.5 MPa

Linear Change on Reheating，（5h,≤2%）:≥1400 ℃

Thermal conductivity（350±25）℃:≤0.55 W/m·K

Page 4 of 5|< << 1 2 3 4 5 >> >|

High Alumina Insulating Brick

Aluminium Silicate Refractory Ceramic Fiber Blanket Heat Resistant Insulation Wool 128kg/M3 Density For Boiler

Anti Stripping Refractory Ceramic Fiber Blanket 6-50mm Thickness Insulation

High Alumina Insulating Brick for Reheating Furnace - 150150150mm

China High Alumina Insulating Brick

SK40 Insulating Refractory Brick Yellow Al2O3 High Alumina Brick

Boiler Furnace High Alumina Insulating Brick Lightweight Slag Resistance

Corundum Refractory Alumina Magnesia Spinel Brick For Industry Furance

Thermal Insulation Al2O3 95% Alumina Ceramic Brick 3.0MPa

Mullite High Alumina Insulating Brick Kilns Refractory Fire Brick Heat Insulation

Furnace Refractory High Alumina Insulating Brick Thermal Processing

Heat Insulation 1350C 0.7g/Cm3 Fire Retardant Bricks

Wear Resistance 0.7g/Cm3 High Alumina Insulating Brick

High Alumina Light Weight 0.8g Pizza Oven Fire Bricks

Industry Furnace 1.2g 1400C High Alumina Insulating Brick

High Strength Cement Kiln 48 Al2O3 High Heat Bricks

1770℃ 2.0 Fe2O3 High Alumina Insulating Brick For Coke Oven

Clay Refractory Brick

High Strength Low Apparent Porosity 1450 Degree Clay Fire Brick

Pizza Oven Light Weight High Density 2.3g Clay Fired Brick

High Thermal Shock Resistance Fe2O3 Clay Refractories Bricks

High Alumina Refractory Bricks

Flint Clay High Alumina Refractory Bricks For Rotary Kiln

high heat Alumina Checker Brick For Hot Blast Stove Of Medium And Large Size Blast Furnace

55% Al2O3 Blast Furnace Bauxite High Alumina Fire Bricks