Bulk Density: ≤1.3 G/cm3
Cold Crushing Strength: ≥5.0 MPa
Cold Crushing Strength: ≥3 MPa
Linear Change On Reheating,(5h,≤2%): ≥1250 ℃
Bulk Density: ≤0.8 G/cm3
Cold Crushing Strength: ≥3 MPa
Bulk Density: ≤1.2 G/cm3
Cold Crushing Strength: ≥4.5 MPa
Bulk Density: ≤0.7 G/cm3
Linear Change On Reheating,(5h,≤2%): ≥1350 ℃
Cold Crushing Strength: ≥4.5 MPa
Linear Change On Reheating,(5h,≤2%): ≥1400 ℃
Cold Crushing Strength: ≥4.5 MPa
Linear Change On Reheating,(5h,≤2%): ≥1400 ℃
Raw Material: High Alumina
Color: Yellow
Bulk Density: ≤0.7 G/cm3
Linear Change On Reheating,(5h,≤2%): ≥1350 ℃
Bulk Density: ≤0.7 G/cm3
Linear Change On Reheating,(5h,≤2%): ≥1350 ℃
AL2O3(%): ≥36
Fe2O3(%): ≤1.0
Working Temperature:: ≤1800
Shape: Brick
Raw Material: Mullite
Al2O3: ≥50%
Raw Material: High Alumina
Color: White
Al2O3 %: ≥50
CaO2 %: ≤0.5
Bulk Density: ≤1.2 G/cm3
Cold Crushing Strength: ≥4.5 MPa