Hot Blast Stove SK37 SK38 SK40 High Temp Fire Brick

Production process:

The production methods of SK37 High Temp Fire Brick and clay bricks are basically the same.

Aluminum oxide (Al2O3) content is higher than 48% SK37 High Temp Fire Brick

A neutral refractory with an alumina content of more than 48%.Made of bauxite or other raw materials of high alumina content after molding and calcining.High thermal stability, refractoriness in 1770℃ above.Good slag resistance, used for lining steelmaking electric furnace, glass furnace, cement converter, etc.

One of the important working properties of SK37 High Temp Fire Brick is the structural strength at high temperatures. The high-temperature creep properties are also measured to reflect the high-temperature structural strength. From the test, we knew that, with the increase of the Al2O3 content, the structural strength also become higher.

When the content of Al2O3 less than 70%, the load softening temperature depends on the quantity ratio between the mullite crystal phase and liquid phase. With the increase in the quantity of mullite, It also increased. Therefore, reducing the content of impurities in the raw materials is beneficial to improve the quality of SK37 High Temp Fire Brick.

High charge soft, SK37 High Temp Fire Bricke is a high grade refractory material made of super grade bauxite, fused corundum and fused mullite.

Feature

1. SK37 High Temp Fire Brick have better thermal conductivity than clay bricks.

2. Because Al2O3 in high aluminum products is high and has less miscellaneous mass, softening temperature under load is higher than clay bricks.

3. The thermal shock resistance of SK37 High Temp Fire Brick is between clay and silica products.

Applications:
 

• Nonferrous Metal Furnace
• Rotary & Shaft Kiln
• Various Incinerator
• Reheating Furnace
• Permanent Lining For EAF Ladle
• General Industrial Furnace etc.

Annec is a national hi-tech company, and is accredited with ISO9001:2008 quality control system standards, ISO12001:2004 environmental control system standards, and GB/T28001-2011 HAZOPS. Annec has set up a thorough and effective management system with practical considerations for her employees and community, and is persistent in promoting employee self-value and product quality. With these efforts, Annec was awarded the prestigious 2012 Zhengzhou Mayor Quality Prize.

Annec has established a strong research and development team, represented by 11 wee known experts including prof. Zhou Gouzhi, an academician of Chinese academy of sciences, Mr. Wu Qichang, Chinese national design master of iron-making engineering. Prof. Zhang Bopeng, Inventor of the top combustion hot blast stove in Shougang Steel. The team possesses a multi-subject crossing and combination superiority in terms of metallurgy, materials science and engineering, thermal engineering, structure engineering, etc. And is beneficial to aim at the front of world steelmaking technology and continuously new technologies and new products to meet challenges of greenization, intelligence and collaboration in steelmaking industry and refractories industry.