Product Details:
|
| Colar: | Red | Shape: | Standard Or Special Shape |
|---|---|---|---|
| Bulk Density: | ≥2.4g/cm2 | Apparent Porosity: | ≤24% |
| Fe2O3: | ≤1.5% | CCS: | ≥60Mpa |
| Refractoriness: | ≥1550℃ | RUL: | ≥1350℃ |
| High Light: | High Alumina Fire Resistant Refractory Brick,Al2o3 Fire Resistant Brick,High Alumina Refractory Brick For Fireplaces |
||
High Alumina Al2O3 Fire Resistant Brick
High Alumina Al2O3 Fire Resistant Brick are produced with selected bauxite chamotte by advanced process and strict quality control. The main mineral components are corundum and mullite phases. Its features are excellent high temperature mechanics and chemical corrosion resistance.
If Al2O3 content is higher than 90%, it is called corundum brick. Due to different resources, national standards are not completely consistent. For example, European countries have stipulated that the lower limit of Al2O3 content for high-alumina refractories is 42%. In China, according to the content of Al2O3 in high alumina bricks, it is usually divided into three grades: Grade I──Al2O3 content>75%; Grade II──Al2O3 content is 60～75%; Grade III──Al2O3 content is 48～60%.
One of the important working properties of High-alumina refractory bricks is the structural strength at high temperatures. The high-temperature creep properties are also measured to reflect the high-temperature structural strength. From the test, we knew that, with the increase of the Al2O3 content, the structural strength also become higher.
When the content of Al2O3 less than 70%, the load softening temperature depends on the quantity ratio between the mullite crystal phase and liquid phase. With the increase in the quantity of mullite, It also increased. Therefore, reducing the content of impurities in the raw materials is beneficial to improve the quality of the High alumina refractory bricks.
Physical and chemical indexes:
Application:
High Alumina Al2O3 Fire Resistant Brick used for lining blast furnaces, hot blast stoves, electric furnace tops, blast furnaces, reverberatory furnaces, and rotary kilns. In addition, high alumina bricks are also widely used as open hearth regenerative checker bricks, plugs for pouring systems, nozzle bricks, etc. However, the price of high alumina bricks is higher than that of clay bricks, so it is not necessary to use high alumina bricks where clay bricks can meet the requirements.
1.Iron&steel making industry:
Blast furnace,hot blast furnace(stove),pellet shaft furnace,hot metal ladle,steel ladle, tundish,heating furnace,soaking pit furnace,heat treatment furnace,refining furnace,reheating furnace,metal mixter furnace,annealing furnace, cupola furnace,electric arc furnace,induction furnace,AOD furnace,VOD furnace,etc thermal technology equipment.
2.Non-ferrous Metal industry:
Smelting furnace,refining furnace,reverberatory furnace,converter furnace.
3.Building materials industry:
Cement kiln,glass kiln,ceramic kiln,lime kilns,kiln car,tunnel kiln
4.Energy & Incineration:Coke oven,general boiler,power,generation,boiler,circulating fluidized bed boiler,electric furnace,carbon rosating furnace,waste incinerators.
5.Others: Petrochemical industry furnace.
Annec has established a strong research and development team, represented by 11 wee known experts including prof. Zhou Gouzhi, an academician of Chinese academy of sciences, Mr. Wu Qichang, Chinese national design master of iron-making engineering. Prof. Zhang Bopeng, Inventor of the top combustion hot blast stove in Shougang Steel. The team possesses a multi-subject crossing and combination superiority in terms of metallurgy, materials science and engineering, thermal engineering, structure engineering, etc. And is beneficial to aim at the front of world steelmaking technology and continuously new technologies and new products to meet challenges of greenization, intelligence and collaboration in steelmaking industry and refractories industry.