Product Details:
|
| Bulk Density: | ≤1.2 G/cm3 | Cold Crushing Strength: | ≥4.5 MPa |
|---|---|---|---|
| Linear Change On Reheating，（5h,≤2%）: | ≥1400 ℃ | Thermal Conductivity（350±25）℃: | ≤0.55 W/m·K |
| Characteristic 1: | Light Weight | Characteristic 2: | Low Thermal Conductivity |
| Al2O3: | ≥48 % | Fe2O3: | ≤2.0 % |
| High Light: | 1400C High Alumina Insulating Brick,1.2G High Alumina Insulating Brick,1400C Industry Furnace Brick |
||
Industry Furnace 1.2g 1400C High Alumina Insulating Brick
Definition:
1. According the shape, High Temp Fire Insulating Brickcan be divided into standard brick, special-shaped brick.
2. According thecharacteristic, High Temp Fire Insulating Brick can be divided into high alumina insulating brick, fire clay insulating brick, Mullite insulating brick, corundum insulating brick, etc.
3. According the application, High Temp Fire Insulating Brick can be divided into building materials for blast furnace, Building materials for coke oven, Building materials for steel making furnace and so on
Advantage:
1. Low bulk density, low thermal conductivity, good thermal insulation performance.
2. Refractory category allow direct contact of fire, suitable ofr various atmosphere
3. Good integrity with furnace lining, long service life, easy operation, could be shaped freely
4. Product specification: standard form, normal standard, shaped and special shaped bricks.
5. Can be used in various kilns because of its cheapness and general tray package. Among all of the refractory materials, it is the most widely used.
Application:
HHigh Temp Fire Insulating Brick is mainly used for the partition of coking chamber and combustor of coke making furnace, regenerator chamber and cinder chamber of steelmaking open hearth furnace, soaking pit, refractory material of glass melting furnace and sintering furnace of ceramics and other kiln vault and other load-bearing parts.
It is also used for high temperature load bearing parts of hot blast furnace and acid open hearth furnace top.
Product Description:
|
High Temp Fire Insulating Brick |
|||
|
Item |
Unit |
LG140-1.2 |
LG140-1.0 |
|
Al2O3 |
% |
≥48 |
≥48 |
|
Fe2O3 |
% |
≤2.0 |
≤2.0 |
|
Bulk Density |
g/cm3 |
≤1.2 |
≤1.0 |
|
Cold Crushing Strength |
Mpa |
≥4.5 |
≥4.0 |
|
Linear Change on Reheating(≤2%) |
℃ |
≥1400 |
≥1400 |
|
Thermal conductivity(350±25)℃ |
W/mK |
≤0.55 |
≤0.50 |
Packaging and shipping
Standard packing: waterproof inner packing + outer packing suitable for container transportation