Product Details:
|
| Bulk Density: | ≤0.8 G/cm3 | Cold Crushing Strength: | ≥3 MPa |
|---|---|---|---|
| Thermal Conductivity（350±25）℃: | ≤0.35 W/m·K | Characteristic 1: | Light Weight |
| Characteristic 2: | Low Thermal Conductivity | Al2O3: | 30-45% |
| High Light: | 0.8g High Temp Fire Brick,45 Al2O3 High Temp Fire Brick,45 Al2O3 Blast Furnaces Fire Brick |
||
45 Al2O3 0.8g High Temp Fire Brick For Blast Furnaces
Standard sizing:This brick is special size for pipes of industry furance ,Special size and OEM Service also provide!
The size is precise, providing kinds of shapes according to customer's drawing
Definition:
Insulating Fire Clay Brick Refractory generally refer to refractory bricks with a density less than 1.3 g/cm3. Due to the characteristics of low density, high porosity, small thermal conductivity, good thermal insulation and certain compressive strength, light-weight refractory bricks have been widely used in heat treatment equipment.
For strength products, high-quality plate-like corundum and mullite are used as aggregates, sillimanite composite is used as a matrix, special additives and a small amount of rare earth oxides are mixed, and then subjected to high-pressure molding and high-temperature firing.
Advantage:
Competitive Price. Make the products competitive in your market.
Abundant Experience. Prevent cracks and twist in bricks.
Different Moulds. Save mould fees for you.
Strict Quality Control. Meet clients’ quality requirement.
Large stocks. Guarantee prompt delivery.
Professional Packing. Avoid damage and secure the goods in transportatio
Application:
Insulating Fire Clay Brick Refractoryis not only widely used in insulating layers of various of thermal processing equipments, such as hot blast furnace, coke oven, glass kiln, etc, but also apply to linings in parts of furnace without strong high-temperature molten material erosive.
Product Description:
|
Insulating Fire Clay Brick Refractory |
|||
|
Item |
NG125-0.8 |
NG120-0.6 |
NG115-0.4 |
|
Bulk Density ( g/cm3) |
≤0.8 |
≤0.6 |
≤0.4 |
|
Cold Crushing Strength (MPa) |
≥3 |
≥2 |
≥1 |
|
Linear Change on Reheating(≤2%) |
≥1250 |
≥1200 |
≥1150 |
|
Thermal conductivity(350±25)℃ (W/mK) |
≤0.35 |
≤0.25 |
≤0.20 |