Product Details:
|
| Product Description: | Fireclay Refractory Brick Based On Chamotte, Fireclay, Ceramic Bond | Molding Method: | Machine Pressed Brick |
|---|---|---|---|
| Al2O3: | 40-55 | Fe2O3: | 0-1.7 |
| Apparent Porosity: | 20-28 | Bulk Density: | 2.1-2.2 |
| Cold Crushing Strength: | 30-60 | 0.2MPa,Refractoriness Under Load: | 1400-1550 |
| Characteristic 1: | High-temperature Endurable | Characteristic 2: | High-temperature Creep Rate Is Low |
| Characteristic 3: | Good Volume Stability At High Temperature | ||
| High Light: | 40 Al2O3 Fire Clay Bricks,1.7 Fe2O3 Fire Clay Bricks,Al2O3 Tunnel Kiln Clay Bricks |
||
Tunnel Kiln Yellow Fireproof Resistant 40 Al2O3 Fire Clay Bricks
Standard sizing:This 230x114x73cm ,Special size and OEM Service also provide!
The size is precise, providing kinds of shapes according to customer's drawing
Definition:
Refractory brick is referred to as fire brick. Refractory made of refractory clay or other refractory materials. Pale yellow or brown. It is mainly used for building smelting furnaces and can withstand high temperatures of 1,580℃-1,770℃. Also called firebrick. Its refractories is usually above 1750 °C.The main mineral components are corundum and mullite phases.It is a kind of neutral refractory material so that it enjoys excellent resistance to acid and alkali corrosion.
According to the preparation process, it can be divided into fired bricks, non-fired bricks, fused bricks (fused cast bricks), refractory and heat insulation bricks; according to the shape and size, it can be divided into standard bricks, ordinary bricks, special-shaped bricks, etc.
Fireproof Resistant Fire Clay Brick is made from clinker clay by mixing, forming, drying, sintering and matching characterized by good resistance to corrosion and abrasion, good thermal shock resistance, good spelling resistance, high mechanical strength, good volume stability under high temperature.
Advantage:
1. High refractoriness,
2. High-temperature endurable.
3. Good corrosion resistance.
4. Good spalling resistance and wear resistance.
5. Good thermal shock resistance.
6. High mechanical strength.
7 .High-temperature creep rate is low.
8. Good volume stability at high temperature.
Application:
Fireproof Resistant Fire Clay Brick can be used to furance contruction,blast furance/hot blast stove,steel foundries,furnace in the nonferrous metal industry,coke oven and gas furnace,galss industry,cement industry,safty lining of ladle and backup lining of boiler
1) Iron&steel making industry.
2) Petrochemical, metallurgical, ceramics, glass industry, the furnace lining insulation.
3) Heat treatment furnace backlash insulation.
4) Non-ferrous metal industry.
5) High temperature reaction, heating equipment back insulation insulation
Product Description:
| Fireproof Resistant Fire Clay Brick | ||||
| Item | Unit | RN-42 | HRN-42 | HRN-48 |
| AL2O3 % | % | ≥42 | ≥42 | ≥48 |
| Fe2O3 % | % | ≤ 1.7 | ≤ 1.7 | ≤ 1.7 |
| Refractoriness | ℃ | ≥1750 | ≥1750 | ≥1750 |
| Bulk density | g/cm3 | ≥2.15 | ≥2.15 | ≥2.35 |
| Apparent porosity | % | ≤ 24/23 | ≤ 24/21 | ≤ 24/21 |
| cold crushing strength | Mpa | ≥30 | ≥40 | ≥40 |
| 0.2MPa,Refractoriness under load,℃ | ℃ | ≥ 1400 | ≥ 1520 | ≥ 1550 |
| Permanent linear change | % | 0～-0.3 | 0～-0.3 | 0～-0.3 |
| thermal shock resistance, ( 1100 ℃ water ) |
cycle | ≥ 20 | ≥30 | ≥40 |