High Temp Anti Acid Alumina Silica Firebrick For Furnace
Standard sizing:This brick is special size for pipes of industry furance ,Special size and OEM Service also provide!
The size is precise, providing kinds of shapes according to customer's drawing
Product Description:
Silica Brick | ||
Item | Value | |
Al2O3 | (%) | ≤1.0 |
Fe2O3 | (%) | ≤1.0 |
SiO2 | (%) | ≥95 |
Bulk Density ( g/cm3) | ≥1.80(Wall Brick) | |
≥1.78(Checker Brick / Hand Brick) | ||
Ture Bulk Density ( g/cm3) | ≤2.34 | |
Apparent Porosity (%) | ≤24(Checker Brick / Hand Brick) | |
≤23(Wall Brick) | ||
Cold Crushing Strength (MPa) | ≥25(Machine-made Brick) | |
≥22(Checker Brick / Hand Brick) | ||
Residual Quartz (%) | ≤1.5 | |
Thermal Expansion1000℃ (%) | 1.2 | |
Thermal conductivity1200℃ (W/mK) | 2 | |
Creep Rate(20~50h ,0.2MPa) (%) | ≤0.3(1500℃) | |
Linear Change on Reheating(1500℃×5h) (%) | 0~+0.2 |
Definition:
Silica Brick s made of silicon as raw material with high temp firing ,which silicon oxide is above 93% ,used in hot blast furnace,coke oven,glass kiln,these brick have good volume stability at high temperature, high refractoriness under the load,small rate of shrinkage in working condition.
It is slowly fired at 1350 ~ 1430℃ in reducing atmosphere. When heated to 1450℃, about 1.5~2.2% of the total volume expansion, the residual expansion will make the cut joints close, to ensure that the masonry has good air tightness and structural strength.
Advantage:
Lower impurity content
Excellent resistance in slag abrasion
No shrink in burn repeatedly
Super higher cold crush strength character
Good performance in high temp refractoriness under load
Higher temperate resistant with good refractoriness
Aluminum silicate refractory brick
Application:
Silica brick is mainly used for coking chamber and combustor of coke making furnace, regenerator chamber and cinder chamber of steel making open hearth furnace, soaking pit, refractory material of glass melting furnace, sintering of ceramic and other kiln storage. Used for furnace partition Other load bearing parts.
It is also used for high temperature load bearing parts of high temperature blast furnaces and the upper part of acid open hearth furnaces.
Silica Brick for glass furnace refers to the silicon refractory product used in the high temperature part of the glass kiln (not in contact with the glass liquid), it is a kind of acid refractory mainly made from tridymite, cristobalite and a small amount of residual quartz as well as glass phase. The raw refractory material is natural silica sand whose SiO2 content should be more than 96%. The higher SiO2 content in silica sand, the higher temperature silica bricks resist.
Glass kiln Silica Brick has high temperature and volume stability, no pollution to glass liquid, chemical corrosion resistance, small bulk density, and can reduce the weight of furnace body.